Phase transformation and reaction kinetics of BaK122 precursor synthesized via a two-step method
1
Key Laboratory of High Density Electromagnetic Power and Systems (Chinese Academy of Sciences), Institute of Electrical Engineering, Chinese Academy of Sciences, 100190, Beijing, China
2
University of Chinese Academy of Sciences, 100049, Beijing, China
3
Institute of Electrical Engineering and Advanced Electromagnetic Drive Technology, Qilu Zhongke, 250013, Jinan, China
4
School of Materials Science and Engineering, Zhengzhou University, 450001, Zhengzhou, China
a
zxp@mail.iee.ac.cn
b
ywma@mail.iee.ac.cn
Received:
23
March
2025
Accepted:
14
April
2025
Published online:
29
April
2025
122-Type iron-based superconductors have gained considerable interest due to their potential for high-field applications. A two-step method for preparing BaK122 precursor powders is shown to enhance the superconducting performance of wires and tapes. However, impurities pose formidable challenges to enhancing critical current density, while their underlying causes remain an open question. In this work, the phase formation process of the two-step precursors was investigated. After sintering at 550 °C, iron arsenides and KFe2As2 are generated in large quantities. The superconducting properties of the sample improve significantly when the sintering temperature is increased to 700 °C. However, the distribution of K and Ba elements in the 122-phase remains inhomogeneous. For the samples sintered at 850 °C, impurities are almost eliminated, resulting in the formation of high-purity Ba0.6K0.4Fe2As2. The reaction mechanisms for each exothermic process follow the Avrami-Erofeev equation and are expressed as G(α) = [− ln(1-α)]1/n, which corresponds to the nucleation and crystal growth model. Based on the above results, we summarize the phase formation process of the two-step BaK122 precursor and propose a formation mechanism for the impurities. This study provides valuable insights into optimizing the sintering process and improving the purity of BaK122 precursors.
Copyright comment Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.
© The Author(s), under exclusive licence to EDP Sciences, SIF and Springer-Verlag GmbH Germany, part of Springer Nature 2025
Springer Nature or its licensor (e.g. a society or other partner) holds exclusive rights to this article under a publishing agreement with the author(s) or other rightsholder(s); author self-archiving of the accepted manuscript version of this article is solely governed by the terms of such publishing agreement and applicable law.